MIG TIG cooper coated solid welding wire ER80s-G
CHARACTERISTICS:
Er80s-g welding wire is 550MPa grade low alloy steel welding wire. CO2 or Ar + CO2 mixed gas protection is used for welding.
The welding process of er80s-g welding wire has less spatter, stable arc and beautiful weld formation.
ATTENTION:
1. Rust, oil, water and other impurities on the weldment must be removed before welding.
2. The welding parameters provided are for reference only,
and the user should formulate the welding specifications suitable for production according to the specific situation.
APPLICATION:
Used for the weathering resistant structure on 500MPa such as vehicle, offshore engineering and .
WELDING POSITION: PA,PB,PC,PD,PE,PF
TYPE OF CURRENT/GAS: DC+/CO2
Typical Chemical Composition Of Deposited Metal(wt%)
C | Mn | Si | P | S | Cu | Cr | Ni | Mo | V | Others |
0.07 | 1.70 | 0.60 | 0.005 | 0.05 | 0.21 | - | - | 0.18 | - | Ti: 0.15 |
Typical Mechanical Properties Of Deposited Metal
Y.P.(MPa) | T.S.(MPa) | E.L.(%) | I.V.(J) | |||
495 | 590 | 28 | -40°C/112 |
Product detail pictures:
Related Product Guide:
The composition of the welding electrode
Every member from our high efficiency sales team values customers' needs and business communication for Reliable Supplier Magic Welding Rod - MIG TIG cooper coated solid welding wire ER80s-G – Tianqiao, The product will supply to all over the world, such as: Irish, Colombia, Brasilia, For more than ten years experience in this filed, our company has gained high reputation from home and abroad. So we welcome friends from all over the world to come and contact us, not only for business, but also for friendship.
By Murray from Pakistan - 2017.02.18 15:54
This is a very professional wholesaler, we always come to their company for procurement, good quality and cheap.
By tobin from Austria - 2018.12.10 19:03