APPLICATIONS:
It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and soon.
CHARACTERISTICS:
THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.
RECAUTIONS:
1. Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.
Chemical Composition of the deposited metal(the mass fraction): %
|
Elements |
C |
Si |
Mn |
S |
Fe |
Ni |
The mass of other elements |
|
Standard value |
≤2.0 |
≤2.5 |
≤1.0 |
≤0.03 |
≤8.0 |
≥90 |
≤1.0 |
Welding reference current: (AC,DC+)
|
Electrode diameter(mm) |
2.5 |
3.2 |
4.0 |
|
Welding current(A) |
60-90 |
90-110 |
120-150 |
Welding distortion correction:
For deformation correction in hot state, mechanical correction and hammering are strictly prohibited in the range of blue brittle temperature (300℃~500℃) to avoid brittle cracks.
Pay attention to the following requirements when the flame is locally heated
It is not advisable to repeat heating at the same part to avoid changes in the metallographic structure and mechanical properties of the steel.
Do not cause repeated corrections of tension and compression in the same part.
For hardenable welded parts, watering and rapid cooling are strictly prohibited.
Welding parts that need to be annealed should be rectified before annealing to eliminate internal stress during annealing. During annealing, the welded parts must be placed steadily so as not to deform again.
The flame straightening heating temperature can be 700℃~850℃ (fuchsia), and should not exceed 900℃ (bright red) for low alloy structural steel.
Product detail pictures:
Related Product Guide:
The composition of the welding electrode
Our pursuit and firm aim should be to Always fulfill our buyer requirements. We carry on to produce and structure top-quality excellent solutions for equally our aged and new consumers and accomplish a win-win prospect for our consumers as well as us for factory Outlets for 308l Stainless Steel - Z308 Pure nickel cast iron electrode GB / T 10044 EZNi-1 AWS ENi-C1 JIS DFCNi – Tianqiao, The product will supply to all over the world, such as: UAE, Juventus, Lahore, Customer satisfaction is our goal. We are looking forward to cooperating with you and providing our best services to suit your needs. We warmly welcome you to contact us and make sure you feel free to contact us. Browse our online showroom to see what we can do for you. And then E-mail us your specs or inquiries today.
By Karen from Italy - 2017.02.28 14:19
The after-sale warranty service is timely and thoughtful, encounter problems can be resolved very quickly, we feel reliable and secure.
By Julia from Ecuador - 2017.06.19 13:51